Material characteristics. 2.1.3.1. The cell dimensions shall be 19 mm ± 10 per cent for each block (see Figure 4). 2.1.3.2. The cells must be made of 3003 aluminium for the upper row. 2.1.3.3. The cells must be made of 5052 aluminium for the lower row. 2.1.3.4. The aluminium honeycomb blocks should be processed such that the force deflection-curve when statically crushed (according to the procedure defined in paragraph 2.1.
Appears in 2 contracts
Sources: Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles, Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles
Material characteristics. 2.1.3.1. The cell dimensions shall be 19 mm ± 10 per cent for each block (see Figure figure 4).
2.1.3.2. The cells must be made of 3003 aluminium for the upper row.
2.1.3.3. The cells must be made of 5052 aluminium for the lower row.
2.1.3.4. The aluminium honeycomb blocks should be processed such that the force deflection-curve when statically crushed (according to the procedure defined in paragraph 2.1.in
Appears in 2 contracts
Sources: Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles, Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles
Material characteristics. 2.1.3.1. The cell dimensions shall be 19 mm ± 10 per cent for each block (see Figure figure 4).
2.1.3.2. The cells must be made of 3003 aluminium for the upper row.
2.1.3.3. The cells must be made of 5052 aluminium for the lower row.
2.1.3.4. The aluminium honeycomb blocks should be processed such that the force deflection-curve when statically crushed (according to the procedure defined in paragraph 2.1.